Microstructural degradation in compound tubes
Publiceringsår
1996
Upphovspersoner
Salonen, Jorma; Auerkari, Pertti
Abstrakt
In order to quantify microstructural degradation at high temperatures, samples of SA 210 / AISI 304 L compound tube material were annealed in the temperature range 540 - 720°C for 1 to 1 000 hours. The hardness of the annealed material was measured and the microstructure of the samples was investigated with optical and scanning electron microscopy. Microstructural degradation was characterised by the carbide structure in the ferritic-pearlitic base material and by the depth of decarburised and carburised zones of the compound tube interface. The observed changes were quantified in terms of their time and temperature dependence and diffusion coefficients of the process. The results can be used in estimating the extent of thermal exposure of high-temperature components after long-term service or after incidences of overheating.
Visa merOrganisationer och upphovspersoner
Teknologiska forskningscentralen VTT Ab
Auerkari Pertti
Publikationstyp
Publikationsform
Separat verk
Målgrupp
Vetenskaplig
Kollegialt utvärderad
Kollegialt utvärderad
UKM:s publikationstyp
C1 Separat utgivet vetenskapligt verkPublikationskanalens uppgifter
Journal
VTT Publications
Förläggare
VTT Technical Research Centre of Finland
Nummer
279
ISSN
ISBN
Öppen tillgång
Öppen tillgänglighet i förläggarens tjänst
Ja
Licens för förläggarens version
Annan licens
Parallellsparad
Nej
Övriga uppgifter
Nyckelord
[object Object],[object Object],[object Object],[object Object],[object Object],[object Object],[object Object],[object Object],[object Object],[object Object],[object Object]
Språk
engelska
Internationell sampublikation
Nej
Sampublikation med ett företag
Nej
Publikationen ingår i undervisnings- och kulturministeriets datainsamling
Nej