Hydrogen embrittlement on fracture resistance of low-alloy reactor pressure vessel steel with high dynamic strain aging at 288 °C
Publiceringsår
2022
Upphovspersoner
Que, Zaiqing; Seifert, H. P.; Mazánová, V.; Spätig, P.
Abstrakt
<p>Fracture mechanics tests in hydrogenated high-temperature water at 288 °C on low-alloy reactor pressure vessel steel with high dynamic strain aging (DSA) susceptibility revealed reduced fracture resistance, accelerated crack growth and increased quasi-cleavage appearance than test in high-temperature air. Hydrogen-induced softening by HESIV and HELP concur in synergy with DSA at 288 °C, which was evidenced by crack-tip microstructural characterisations.</p>
Visa merOrganisationer och upphovspersoner
Teknologiska forskningscentralen VTT Ab
Que Zaiqing
Publikationstyp
Publikationsform
Artikel
Moderpublikationens typ
Tidning
Artikelstyp
En originalartikel
Målgrupp
VetenskapligKollegialt utvärderad
Kollegialt utvärderadUKM:s publikationstyp
A1 Originalartikel i en vetenskaplig tidskriftPublikationskanalens uppgifter
Journal
Volym
308
Artikelnummer
131269
ISSN
Publikationsforum
Publikationsforumsnivå
1
Öppen tillgång
Öppen tillgänglighet i förläggarens tjänst
Ja
Öppen tillgång till publikationskanalen
Delvis öppen publikationskanal
Licens för förläggarens version
CC BY
Parallellsparad
Nej
Övriga uppgifter
Vetenskapsområden
Maskin- och produktionsteknik; Materialteknik
Nyckelord
[object Object],[object Object],[object Object],[object Object]
Språk
engelska
Internationell sampublikation
Ja
Sampublikation med ett företag
Nej
DOI
10.1016/j.matlet.2021.131269
Publikationen ingår i undervisnings- och kulturministeriets datainsamling
Ja