SCC behaviour of laser powder bed fused 316L stainless steel in high-temperature water at 288 °C
Publiceringsår
2023
Upphovspersoner
Que, Zaiqing; Riipinen, Tuomas; Goel, Sneha; Revuelta, Alejandro; Saario, Timo; Sipilä, Konsta; Toivonen, Aki
Abstrakt
Stress corrosion cracking (SCC) behaviour of laser powder bed fused stainless steel 316L was evaluated with U-bend testing in oxygenated high-temperature water at 288 °C. The effects of solution annealing temperature (1066, 1150 and 1200 °C), surface finish (as-built and wire cut) and the sample orientations on the SCC behaviour were studied. The results show that a higher annealing temperature introduces further recrystallization, coarsening of the oxide inclusions and a decrease in resistance to SCC. A wire cut surface leads to a higher susceptibility to SCC than the as-built surface. Sample orientation was found not to affect the SCC susceptibility.
Visa merOrganisationer och upphovspersoner
Teknologiska forskningscentralen VTT Ab
Toivonen Aki
Sipilä Konsta
Goel Sneha
Saario Timo
Riipinen Tuomas
Que Zaiqing
Publikationstyp
Publikationsform
Artikel
Moderpublikationens typ
Tidning
Artikelstyp
En originalartikel
Målgrupp
VetenskapligKollegialt utvärderad
Kollegialt utvärderadUKM:s publikationstyp
A1 Originalartikel i en vetenskaplig tidskriftPublikationskanalens uppgifter
Öppen tillgång
Öppen tillgänglighet i förläggarens tjänst
Ja
Öppen tillgång till publikationskanalen
Delvis öppen publikationskanal
Licens för förläggarens version
CC BY
Parallellsparad
Nej
Övriga uppgifter
Vetenskapsområden
Materialteknik
Nyckelord
[object Object],[object Object],[object Object],[object Object],[object Object],[object Object]
Språk
engelska
Internationell sampublikation
Nej
Sampublikation med ett företag
Nej
DOI
10.1016/j.corsci.2023.111022
Publikationen ingår i undervisnings- och kulturministeriets datainsamling
Ja